Aluminum steel pipe

Pipe Type: Aluminum alloy round tube, aluminum alloy square tube, aluminum alloy rectangular tube, aluminum alloy hexagonal tube, high precision ultra-fine ultra-thin aluminum tube
Outside Diameter: 1/2’’mm - 750mm
Thickness: ≥0.3mm

Classification :

Alloy Steel Pipe

+8613787191317

info@northsteelgroup.com

E-mail

Description

Pipe Type: Aluminum alloy round tube, aluminum alloy square tube, aluminum alloy rectangular tube, aluminum alloy hexagonal tube, high precision ultra-fine ultra-thin aluminum tube

Outside Diameter: 1/2’’mm - 750mm

Thickness: ≥0.3mm

MOQ: 1 Ton

Grade：1000,2000,3000,5000,6000,7000 series.

Material:1015, 1060, 2011, 2014, 2017, 2024, 3003, 5005, 5052, 5154, 5056, 6106, 6201, 6011, 6351, 6060, 6063, 6061, 6005, 6082, 6463, 6262, 7003, 7075, 7050, 7005, etc

Type: Extruded, Welded, Extruded Seamless, Cold Drawn.
Shape: Round, Square, Rectangle.

Manufacturing Technique: Hot Rolled, Cold Drawn, Cold Rolled, Forged.

Standard: AISI, ASTM, JIS, GB, DIN, etc. Related Standard: ASTM B210 / B210M, ASTM B241 / B241M, ASTM B221/ B221M, ASTM B 211 ASME SB 211 / ASTM B 619 ASME SB 619.etc

Surface: Mill, polished, bright, hair line, brush

Color:Silver, White,Bronze,Gold,Black,Champagne, Or customized
Film Thickness:Anodized:12-25 μm,Powder coating:40-80 μm

Aluminium Alloy Seamless Pipes
Aluminum 2014 | 2024 | 6061 | 6082 | 7075 Seamless pipes, Aluminum Alloy Seamless Pipe

Aluminum Welded Pipes
Aluminium & Aluminium Alloy 2014, 2024, 6061, 6082, 7075 Welded Pipes Supplier, Aluminum ERW Pipe

Aluminum Round Pipes & Tubes
Aluminium 2014 | 2024 | 6061 | 6082 | 7075 Round Pipes, Aluminum Alloy Round Tubes, Aluminum and Aluminum-Alloy Round Pipe

Aluminum Square Pipes & Tubes
Aluminium 2014 | 2024 | 6061 | 6082 | 7075 Square Pipes, Aluminum Alloy Square Tubes, Aluminum and Aluminum-Alloy Square Pipe

Aluminum Rectangular Pipes & Tubes
Aluminium 2014 | 2024 | 6061 | 6082 | 7075 Rectangular Pipes, Aluminum Alloy Rectangular Hollow Tubes, Aluminum Rectangle Pipe

Aluminum Hexagonal Pipes & Tubes
Aluminium Alloy 2014 | 2024 | 6061 | 6082 | 7075 Hexagonal Pipe, Aluminium Hexagonal Tubes, Aluminum Hex Pipes

Specification

Aluminium Pipe Weight Calculation Formula

Weight = l / 1000 * w / 1000 * t * η

l = length in mm
w = width in mm
t = thickness in mm
η = Specific material density ( e.g.: steel = 7.85 kg / dm³)

Aluminium Pipe Size Chart
Manufacturer and supplier of Aluminium Hollow Pipe, Aluminium Gi Pipe in China, view 1/2 Aluminium Pipe weight chart & 3/4 Inch Aluminium Pipe dimensions

OM SIZE	OUTSIDE DIA (D)	WALL THICKNESS IN MM (T)							METRIC SIZE
OM SIZE	OUTSIDE DIA (D)	SCH 10S	SCH 10	SCH 40 S	STD Weight	SCH 40	SCH 80s	SCH 80	METRIC SIZE
1/4 "	13.72	1.65		2.24	2.24	2.24	3.02	3.02	-
3/8"	17.15	1.65		2.31	2.31	2.31	3.2	3.2
1/2"	21.34	2.11	-	2.77	2.77	2.77	3.73	3.73	15
3/4"	26.67	2.11		2.87	2.87	2.87	3.91	3.91	20
1"	33.4	2.77	-	3.38	3.38	3.38	4.55	4.55	25
1 1/4"	42.16	2.77		3.56	3.56	3.56	4.85	4.85	32
1 1/2"	48.26	2.77		3.68	3.68	3.68	5.08	5.08	40
2"	60.32	2.77	-	3.91	3.91	3.91	5.54	5.54	50
2 1/2"	73.02	3.05	-	5.16	5.16	5.16	7.01	7.01	65
3"	88.9	3.05	-	5.49	5.49	5.49	7.62	7.62	80
3 1/2"	101.6	3.05	-	5.74	5.74	5.74	8.08	8.08	90
4"	114.3	3.05	-	6.02	6.02	6.02	8.56	8.56	100
5"	141.3	3.4	-	6.55	6.55	6.55	9.52	9.52	125
6"	168.27	3.4	-	7.11	7.11	7.11	10.97	10.97	150
8"	219.07	3.76	-	8.18	8.18	8.18	12.7	12.7	200
10"	273.05	4.19	-	9.27	9.27	9.27	12.7	15.08	250
12"	323.85	4.57	-	9.52	9.52	10.31	12.7	17.47	300
14"	355.6	4.77	6.35	-	9.52	11.12	-	19.05	350
16"	404.6	4.77	6.35	-	9.52	12.7	-	21.44	400
18"	457.2	4.77	6.35	-	9.52	14.27	-	23.82	450

Physical Property of 1050 1060 1070 aluminum tube pipe

Physical Property of 1050 1060 1070 aluminum tube pipe
Alloy	Temper	Wall thickness /mm	Room temperature Test Result
			Tension Strength/MPa	Yield Strength/MPa	Elongation/%
			Tension Strength/MPa	Yield Strength/MPa	A_50mm	A
			Not less than
1050	O、H111	All	60 ~ 100	20	25	23
	H112	All	60	20	25	23
	F	All	－	－	－	－
1060	O	All	60 ~ 95	15	25	22
1060	H112	All	60	－	25	22
1070	O	All	60 ~ 95	－	25	22
1070	H112	All	60	20	25	22

2014 2017 2024 2A12 Aluminum Tube Pipe

Physical Property of 2014 2017 2024 2A12 Aluminum Tube Pipe
Alloy	Temper	Wall thickness /mm	Room temperature Test Result
			Tension Strength/MPa	Yield Strength/MPa	Elongation/%
			Tension Strength/MPa	Yield Strength/MPa	A_50mm	A
			Not less than
2014	O	all	≤205	≤125	12	10
	T4、T4510、T4511	all	345	240	12	10
	T4、T4510、T4511	all	345	240	12	10
	T42	all	345	200	12	10
	T62	≤18	415	365	7	6
	T62	>18	415	365	-	6
	T6、T6510、T6511	≤12.50	415	365	7	6
		12.50~18.00	440	400	-	6
		>18.00	470	400	-	6
2017	O	all	≤245	≤125	16	16
	T4	all	345	215	12	12
	T1	all	335	195	12	-
2024	O
	T3、T3510、T3511	≤6.30	395	290	10	-
		>6.30~18.00	415	305	10	9
		>18.00~35.00	450	315	-	9
		>35.00	470	330	-	7
2024	T4	≤18.00	395	260	12	10
	T4	>18.00	395	260	-	9
	T42	≤18.00	395	260	12	10
		>18.00~35.00	395	260	-	9
		>35.00	395	260	-	7
	T81、T8510、 T8511	>1.20~6.30	440	260	4	-
		>6.30~35.00	455	260	5	4
		>35.00	455	260	-	4
2A12	O	all	≤245	-	-	10
	T42	all	390	255	-	10
	T4	all	390	255	-	10

Chemical Composition of 2014 2017 2024 2A12 Aluminum Tube Pipe
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ga	V	Ti	Other	Min.Al
2014	0.50-1.2	0.7	3.9-5.0	0.40-1.2	0.20-0.8	0.10	-	0.25	-	-	0.15	0.15	Remainder
2017	0.20-0.8	0.7	3.5-4.5	0.40-1.0	0.40-1.0	0.10	-	0.25	-	-	-	0.15	Remainder
2024	0.50	0.50	3.8-4.9	0.30-0.9	1.2-1.8	0.10	-	0.25	-	-	0.15	0.15	Remainder
2A12	0.5-1.2	0.70	3.9-5.0	0.4-1.2	0.2-0.8	0.10	-	0.25	-	-	0.15	0.15	Remainder

2219 2A11 2A14 2A50 Aluminum Tube Pipe

Chemical Composition of 2219 2A11 2A14 2A50 Aluminum Tube Pipe
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ga	V	Ti	Other	Min.Al
2219	0.20	0.30	5.8-6.8	0.20-0.40	0.02	-	-	0.10	-	-	0.02-0.10	0.15	Remainder
2A11	0.7	0.70	3.8-4.8	0.40-0.8	0.4-0.8	-	0.10	0.30	-	-	0.15	0.15	Remainder
2A14	0.6-1.2	0.7	3.9-4.8	0.4-1.0	0.4-0.8	-	0.10	0.30	-	-	0.10	0.15	Remainder
2A50	0.7-1.2	0.7	1.8-2.6	0.4-0.8	0.4-0.8	-	0.10	0.30	-	-	0.15	0.15	Remainder

Physical Property of 2219 2A11 2A14 2A50 Aluminum Tube Pipe
Alloy	Temper	Wall thickness /mm	Room temperature Test Result
			Tension Strength/MPa	Yield Strength/MPa	Elongation/%
			Tension Strength/MPa	Yield Strength/MPa	A_50mm	A
			Not less than
2219	O	all	≤220	≤125	12	10
	T31、T3510、T3511	≤12.50	290	180	14	12
	T31、T3510、T3511	>12.50~80.00	310	185	-	12
	T62	≤25.00	370	250	6	5
	T62	>25.00	370	250	-	5
	T81、T8510、T8511	≤80.00	440	290	6	5
2A11	O	all	≤245	-	-	10
2A11	T1	all	350	195	-	10
2A14	T6	all	430	350	6	-
2A50	T6	all	380	250	-	10

3003 3A21 Aluminum Tube Pipe

Chemical Composition of 3003 3A21 Aluminum Tube Pipe
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ca	V	Ti	Other	Min.A1
3003	0.6	0.7	0.05-0.2	1.0-1.5	-	-	-	0.1	-	-	-	0.15	Remainder
3A21	0.6	0.7	0.20	1.0-1.6	0.05	-	-	0.15	-	-	0.10-0.20	0.15	Remainder

Physical Property of 3003 3A21 Aluminum Tube Pipe
Alloy	Temper	Wall thickness /mm	Room temperature Test Result
			Tension Strength/MPa	Yield Strength/MPa	Elongation/%
			Tension Strength/MPa	Yield Strength/MPa	A_50mm	A
			Not less than
3003	O	All	95 ~ 130	35	25	22
	H112	≤1.60	95	35	－	－
	H112	>1.60	95	35	25	22
	F	All	－	－	－	－
3A21	H112	All	≤165	－	－	－

5052 5083 5086 5154 5454 5456 aluminum tube pipe

Chemical Composition
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ga	V	Ti	Other	Min.Al
5052	0.25	0.40	0.10	0.10	2.2-2.8	0.15-0.35	-	0.10	-	-	-	0.15	Remainder
5083	0.40	0.40	0.10	0.40-0.10	4.0-4.9	0.05-0.25	-	0.25	-	-	0.15	0.15	Remainder
5086	0.40	0.50	0.10	0.20-0.7	3.5-4.5	0.05-0.25	-	0.25	-	-	0.15	0.15	Remainder
5154	0.50	0.50	0.10	0.50	3.1-3.9	0.25	-	0.20	-	-	0.20	0.15	Remainder
5454	0.25	0.40	0.10	0.50-1.0	2.4-3.0	0.05-0.20	-	0.25	-	-	0.20	0.15	Remainder
5456	0.25	0.40	0.10	0.50-1.0	4.7-5.5	0.05-0.20	-	0.25	-	-	0.20	0.15	Remainder

Physical Property
Alloy	Temper	Wall thickness /mm	Room temperature Test Result
			Tension Strength/MPa	Yield Strength/MPa	Elongation/%
			Tension Strength/MPa	Yield Strength/MPa	A_50mm	A
			Not less than
5052	O	All	170 ~240	70	15	17
	H112	All	170	70	13	15
	F	All	-	-	-	-
5083	O	All	270~350	110	14	12
	H111	All	275	165	12	10
	H112	All	270	110	12	10
	F	All	-	-	-	-
5154	O	All	205~285	75	-	-
5154	H112	All	205	75	-	-
5454	O	All	215~285	85	14	12
	H111	All	230	130	12	10
	H112	All	215	85	12	10
5456	O	All	285~365	130	14	12
	H111	All	290	180	12	10
	H112	All	285	130	12	10
5086	O	All	240~315	95	14	12
	H111	All	250	145	12	10
	H112	All	240	95	12	10
	F	All	-	-	-	-

6005 6105 6041 6042 aluminum tube pipe

Chemical Composition
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ga	V	Ti	Other	Min.Al
6005	0.6-0.9	0.35	0.10	0.10	0.40-0.60	0.10	-	0.10	-	-	0.10	0.15	Remainder
6105	0.6-1.0	0.35	0.10	0.10	0.45-0.8	0.1	-	0.1	-	-	0.1	0.15	Remainder
6041	0.5-0.9	0.15-0.70	0.15-0.60	0.05-0.20	0.8-1.2	0.05-0.15	-	0.25	-	-	0.15	0.15	Remainder
6042	0.5-1.2	0.70	0.2-0.6	0.40	0.7-1.2	0.04-0.35	-	0.25	-	-	0.15	0.15	Remainder

Physical Property
Alloy	Temper	Wall thickness /mm	Room temperature Test Result
			Tension Strength/MPa	Yield Strength/MPa	Elongation/%
			Tension Strength/MPa	Yield Strength/MPa	A_50mm	A
			Not less than
6005	T1	≤12.50	170	105	16	14
	T5	≤3.20	260	240	8	-
	T5	3.20~25.00	260	240	10	9
6105	T1	≤12.50	170	105	16	14
6105	T5	≤12.50	260	240	8	7
6041	T5、T6511	10.00~50.00	310	275	10	9
6042	T5、T6511	10.00~12.50	260	240	10	-
6042	T5、T6511	12.50~50.00	290	240	-	9

6061 6351 6082 Aluminum Tube Pipe

Chemical Composition of 6061 6351 6082 Aluminum Tube Pipe
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ga	V	Ti	Other	Min.Al
6061	0.40-0.80	0.7	0.15-0.40	0.15	0.8-1.2	0.04-0.35	-	0.25	-	-	0.1	0.15	Remainder
6351	0.7-1.3	0.50	0.10	0.4-0.8	0.4-0.8	-	-	0.20	-	-	0.20	0.15	Remainder
6082	0.7-1.1	0.5	0.1	0.1-0.45	0.6-1.0	0.25	-	0.20	-	-	0.15	0.15	Remainder

Physical Property of 6061 6351 6082 Aluminum Tube Pipe
Alloy	Temper	Wall thickness /mm	Room temperature Test Result
			Tension Strength/MPa	Yield Strength/MPa	Elongation/%
			Tension Strength/MPa	Yield Strength/MPa	A_50mm	A
			Not less than
6061	O	all	170	105	16	14
	T1	≤16.00	260	240	8	-
	T42	all	180	85	16	14
	T62	≤6.30	260	240	8	-
	T62	>6.30	260	240	10	9
	T4、T4510、T4511	all	180	110	16	14
	T51	≤16.00	240	205	8	7
	T6、T6510、T6511	≤6.30	260	240	8	-
	T6、T6510、T6511	>6.30	260	240	10	9
	F	all	-	-	--	-
6351	O、H111	≤25.00	≤160	≤110	12	14
	T4	≤19.00	220	130	16	14
	T6	≤3.20	290	255	8	-
	T6	>3.20--25.00	290	255	10	9
6082	O、H111	≤25.00	≤160	≤110	12	14
	T4	≤25.00	205	110	12	14
	T6	≤5.00	290	250	6	8
	T6	>5.00--25.00	310	260	8	10

6162 6262 6064 6063 6066 6A02 aluminum tube pipe

Chemical Composition
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ga	V	Ti	Other	Min.Al
6162	0.4-0.8	0.5	0.2	0.1	0.7-1.1	-	-	0.25	-	-	0.1	0.15	Remainder
6262	0.4-0.8	0.7	0.15-0.40	0.15	0.8-1.2	0.04-1.4	-	0.25	-	-	0.15	0.15	Remainder
6064	0.4-0.8	0.70	0.15-0.40	0.15	0.80-1.2	0.25	-	0.25	-	-	0.15	0.15	Remainder
6063	0.2-0.6	0.35	0.10	0.10	0.45-0.9	0.10	-	0.25	-	-	0.10	0.15	Remainder
6066	0.9-1.8	0.50	0.7-1.2	0.6-1.1	0.8-1.4	0.4	-	0.25	-	-	0.2	0.15	Remainder
6A02	0.5-1.2	0.5	0.2-0.6	0.15	0.45-0.9	-	-	0.20	-	-	0.15	0.15	Remainder

Physical Property
Alloy	Temper	Wall thickness /mm	Room temperature Test Result
			Tension Strength/MPa	Yield Strength/MPa	Elongation/%
			Tension Strength/MPa	Yield Strength/MPa	A_50mm	A
			Not less than
6162	T5、T5510、T5511	≤25.00	255	235	7	6
	T6、T6510、T6511	≤6.30	260	240	8	－
	T6、T6510、T6511	>6.3-12.50	260	240	10	9
6262	T6、T6511	all	260	240	10	9
6063	O	all	≤130	-	18	16
	T1	≤12.50	115	60	12	10
	T1	>12.50~25.00	110	55	-	10
	T42	≤12.50	130	70	14	12
	T42	>12.50~25.00	125	60	-	12
	T4	≤12.50	130	70	14	12
	T4	>12.50~25.00	125	60	-	12
	T5	≤25.00	175	130	6	8
	T52	≤25.00	150-205	110-170	8	7
	T6	all	205	170	10	9
	T66	≤25.00	245	200	8	10
	F	all	-	-	-	-
6064	T6、T6511	10.0-50.0	260	240	10	9
6066	O	all	≤200	≤125	16	14
	T4、T4510、T4511	all	275	170	14	12
	T42	all	275	165	14	12
	T62	all	345	290	8	7
	T6、T6510、T6511	all	345	310	8	7
6A02	O	all	≤145	-	-	17
	T4	all	205	-	-	14
	T62	all	295	-	-	8
	T6	all	295	-	-	8

7050 7075 7178 aluminum tube pipe

Chemical Composition of 7050 7075 7178 Aluminum Tube Pipe
Alloy	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ga	Zr	Ti	Other	Min.Al
7050	0.12	0.15	2.0-2.6	0.10	1.9-2.6	0.01	-	5.7-6.7	-	0.08-0.15	0.06	0.15	Remainder
7075	0.40	0.50	1.2-2.0	0.30	2.1-2.9	0.18-0.28	-	5.1-6.1	-	-	0.20	0.15	Remainder
7178	0.40	0.50	1.6-2.4	0.3	2.4-3.1	0.18-0.28	-	6.3-7.3	-	-	0.20	0.15	Remainder

Physical Property of 7050 7075 7178 Aluminum Tube Pipe
Alloy	Temper	Wall thickness /mm	Room temperature Test Result
			Tension Strength/MPa	Yield Strength/MPa	Elongation/%
			Tension Strength/MPa	Yield Strength/MPa	A_50mm	A
			Not less than
7050	T76510	all	545	475	7	-
	T73511	all	485	415	8	7
	T74511	all	505	435	7	-
7075	O、H111	≤10.00	≤275	≤165	10	10
	T62	≤6.30	540	485	7	-
		>6.30-12.50	560	505	7	6
		>12.50-70.00	560	495	7	6
	T6、T6510、T6511	≤6.30	540	485	7	-
		>6.30-12.50	560	505	7	-
		>12.50-70.00	560	495	-	6
	T73、T73510、T73511	1.60-6.30	470	400	5	7
		>6.30-35.00	485	420	6	8
		>35.00-70.00	475	405	-	8
7178	O	all	≤275	≤165	10	9
	T6、T6510、T6511	≤1.60	565	525	-	-
		>1.6-6.30	580	525	5	-
		>6.30-35.00	600	540	5	4
		>35.00-60.00	580	515	-	4
		>60.00-80.00	565	490	-	4
	T62	≤1.60	545	505	-	-
		>1.6-6.30	565	510	5	-
		>6.30-35.00	595	530	5	4
		>35.00-60.00	580	515	-	4
		>60.00-80.00	565	490	-	4

Comparison of Alloy Designations for Aluminum Products

Alloy Series	Chinese Standard	American Standard	European Standard
5xxx Series	5052	5052	EN AW-5052
	5083	5083	EN AW-5083
	5754	-	EN AW 5754
6xxx Series	6005	6005	-
	6060	6060	EN AW-6060
	6061	6061	EN AW-6061
	6063	6063	EN AW-6063
	6082	6082	EN AW-6082
	6463	6463	-

Production Process